PVC compounds
PTT-105002
Polyvinyl chloride compound is used for manufacturing of automobile wires as well as of insulation and sheaths of other heat-resistant cable articles.
And at the same time this compound is characterized with higher heat-, benzine-, oil-resistance, it is especially designed for automobile wires.
Medical Certificate applied.
| No. | Technical characteristics | Standard |
|---|
| 1 | Hardness at 20°C, MPa, not more | 2,2 |
| 2 | Tensile strength, MPa, not less | 20,0 |
| 3 | Relative elongation at tensile strength, %, not less | 280 |
| 4 | Specific volume electric resistance at 20°C, Ohm·cm, not less | 5,0·1013 |
| 5 | Combustibility by oxigen index (OI), not less | 22 |
| 6 | Softening temperature, °C | 180 |
| 7 | Relative elongation at tensile strength after endurance, %, not less:
- in petrol at 20°C during 48 hours
- in oil at 120°C during 48 hours
- at 136°C during 7 days |
80
60
90 |